Quick Details
Packaging & Delivery
Quantity(Prices) |
Est.Time(days) |
Usage | Polyurethane |
A/B Materials Temperatures (℃) | 30~35/35~40 |
A+C/B Mix ratio (By weight) | 100/109-111 |
Cream Time (s) | 7~9 |
End of Rise Time (s) | 50~60 |
Free Rise Foam Density(g/cm3) | 0.18-0.23 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | 5~7 |
Molded Density (g/cm3) | 0.40-0.50 |
Hardness (Shore C ) | 45-60 |
Characteristic: Low density, good dimension stability | |||||||
Application: Outsole | |||||||
Typical properties of PU matrix | |||||||
Name of products | Appearance | Viscosity (mPa·s/40℃) | Density (g·cm-3/40℃) | Package(kg) | / | ||
A-1700 | cream white liquid | 500~800 | 1.01~1.02 | 18 | |||
B-5300 | Yellowish Transparent liquid or waxy | 300~600 | 1.08~1.2 | 20 | |||
Materials preheat | |||||||
A-1700: preheated at 50~60℃ for 2~4 hours. | |||||||
B-5300: preheated at 60~70℃ for 10~15 hours. | |||||||
Typical processing parameters & Reaction parameter | |||||||
Items | A/B Materials Temperatures | A+C/B Mix ratio | Cream Time (s) | End of Rise Time (s) | Free Rise Foam Density(g/cm3) | Mold Temperature(℃) | Demold Time(min) |
Parameter | 30~35/35~40 | 100/109-111 | 7~9 | 50~60 | 0.18-0.23 | 45~55 | 5~7 |
The adding content of C-2 should be 380g±20g/18kg. | |||||||
The adding content of water should be 0~90g/18kg according to the reality. | |||||||
The adding content of water should be 0~600g/18kg according to the reality. | |||||||
Physical properties | |||||||
Items | Molded Density (g/cm3) | Hardness | Tensile strength | Elongation (%) | Tear Strength | 168h, 70℃, 95%r.h. hydrolysis |
|
| |||||||
Physical properties | 0.40-0.50 | 45-60 | 2.3-5.2 | 320-410 | 18~26 | >90 |
|
Demold time may be prolonged with the increase of sole thickness. | |||||||
These physical data are acquired by testing a sample of 6mm thick. | |||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Company video and photos
Business Type | Manufacturer, Trading Company | Main Products | PU Resin for Synthetic Leather,PU Resins for Shoe Sole,Polyester Polyol,Adhesive for flexing package,Hot melt adhesive |
Total Employees | Above 1000 People | Year Established | 2007 |
Total Annual Revenue | US$50 Million - US$100 Million | ||
Certifications | -- | Product Certifications | Taicang port area of science and technology innovation advanced enterprise 2008,Top 10 strong private enterprises,SuZhou Domestically R&D institution |
Trademarks | XuChuan | Patents | -- |