Quick Details
Packaging & Delivery
Quantity(Prices) |
Est.Time(days) |
Viscosity(mPa.s/85 ℃) | 1800-2000 |
NCO% content | 3.60-3.80 |
Package(kg) | 20 / 200 |
MOCA Level(%) | 10.8 |
Recommended % Theory(%) | 95 |
Prepolymer Temperature(℃) | 75-85 |
Curative Temperature(℃) | 110-120 |
Pot Life(mins) | 10 |
Demould Time(@ 100°C (hrs)) | 1 |
Post Cure Time(@ 100°C (hrs)) | 10 |
1,This product is a polyester polyol and toluene diisocyanate (T-100) in the synthesis of polyester polyurethane prepolymer.
2,Features: excellent wear resistance, oil resistance, mechanical properties.
3,Uses: Sieve, machinery parts, sealing ring, PU roller and other products.
4,Product Specifcation:
Name of products | Appearances | Viscosity(mPa.s/85 ℃) | NCO% content | Package(kg) |
XCPU-E136 | solid | 1800-2000 | 3.60-3.80 | 20 / 200 |
5,Mixing and Curing Conditions:
MOCA Level | Recommended | Prepolymer | Curative Temperature | Pot Life | Demould Time | Post Cure Time |
% | % | ℃ | ℃ | mins | @ 100°C(hrs) | @ 100°C(hrs) |
10.8 | 95 | 75-85 | 110-120 | 10 | 1 | 10 |
6,Processing Procedure:
Prepolymer at 75 ~ 85 ℃ preheating, after vacuum degassing, the
melt MOCA good homogeneous mixing, deaeration, pouring, molding,
vulcanization molding, stripping, vulcanization.
7,Physical Properties:
Properties presented below are to be used as a guide and not intended
for specification purposes.
Hardness | Tensile Strength | 100% Modulus | 300% Modulus | Angle Tear Strength, | Trouser Tear Strength | Elongation | Resilience | DIN Abrasion | Cured Specific |
Shore A | MPa | MPa | MPa | kN/m | kN/m | % | % | mm3 | g/cm3 |
85 | 48 | 4.2 | 3.8 | 75 | 34 | 670 | 39 | 40 | 1.26 |
Precautions:
1, The product is easy to absorb moisture, will lead to product deterioration in the transportation, storage and use shall be kept sealed packaging good, original sealed storage for six months after opening, to be used up as quickly as possible to prevent moisture absorption metamorphism; If you can not run out of time, to be purged with nitrogen and sealed.
2, The information listed in this specification, may be due to product renewal and change, in view of processing technology, formulation and processing and other applications Not the same, pre-test their applicability in case of application of the product, please contact the
XUCHUAN chemical research and development or technical service department.
Company video and photos
Business Type | Manufacturer, Trading Company | Main Products | PU Resin for Synthetic Leather,PU Resins for Shoe Sole,Polyester Polyol,Adhesive for flexing package,Hot melt adhesive |
Total Employees | Above 1000 People | Year Established | 2007 |
Total Annual Revenue | US$50 Million - US$100 Million | ||
Certifications | -- | Product Certifications | Taicang port area of science and technology innovation advanced enterprise 2008,Top 10 strong private enterprises,SuZhou Domestically R&D institution |
Trademarks | XuChuan | Patents | -- |